| Performance Testing method unit numerical value |
| Melt mass flow rate(230ºC2.16kg) GB/T 3682.1-2018 g/10min 16.8 |
| density ISO 1183 1 g/cm³ |
| Tensile yield stress ISO 527-2 Mpa |
| Tensile yield strain ISO 527-2 % |
| Flexural modulus ISO 178 Mpa 1440 |
| Notched impact strength(23ºC) GB/T 1043.1-2008 KJ/M² 2.1 |
| Rockwell hardness ASTM D785 R scale |
| Load deformation temperature(0.45Mpa) ISO 75 2/B ºC |
| Haze ASTM MA1703 1 % |
| Glossiness ASTM MA1702 1 |
| (1) Typical value: Not a product specification |
| Recommended processing temperature |
| Melting temperature ºC |
PP specific gravity 0.9-0.91 grams/cubic centimeter; molding shrinkage rate; 1.0-25%; molding temperature: 160-220ºC, low density, strength, rigidity, hardness, heat resistance are all superior to low-pressure chairs, can be used at about 100 degrees. It has good electrical properties and high-frequency insulation (not affected by humidity), but it becomes brittle, not wear, and easy to age at low temperatures. It is suitable for making general mechanical parts, corrosion-resistant parts, and insulating parts.